Structural Parts 65% ZrO2 Zirconium Silicate Polishing Ball B125
DESCRIPTION
The main component of Polishing Zirconium Silicate Ball SiO2 ZrO2 B125 is zirconia, which is mainly used for surface treatment such as sand blasting and shot peening. The production process of ceramic shot is to melt high-quality imported zircon sand into liquid at high temperature, and then spray it into balls. The zirconia ceramic spheres are sieved and removed by magnetic separation to obtain particles with high roundness, high strength and uniform particle size. The spherical particles of ceramic shot can achieve better surface brightness during sandblasting, while the workpiece itself does not change color. It is widely used for sandblasting and surface treatment of aviation parts, stainless steel plates, structural parts, stainless steel kitchenware, medical devices,mobile phone / laptop shell, automobile chassis / engine, sports equipment and other industries.
APPLICATION
Electronic equipment field: ceramic shot is used for sandblasting the shells of mobile phones, tablet computers and watches made of aluminum alloy or stainless steel. It can adjust the roughness and gloss of the surface as required, and has the characteristics of anti fingerprint.
Kitchen utensils industry: it is used for sandblasting of high-quality stainless steel cookware, pot bottom, soup spoon and other products, giving the products delicate metal texture and certain antibacterial ability.
Glass products industry: used for atomization treatment of glass, replacing hydrofluoric acid chemical etching process to prevent pollution.
Shot peening of aviation parts: used to improve the fatigue resistance of carbon steel, titanium alloy, aluminum alloy and other aviation mechanical parts and eliminate surface stress. It can be used for surface strengthening of aircraft wings, aeroengine turbine blades, turbine discs, gears and landing gear.
Performance Parameter
| No. |
Parameter |
Value |
| 1 |
Color |
White |
| 2 |
Shape |
sphere/Bead/Ball |
| 3 |
Production technology |
melting method |
| 4 |
Chemical composition |
ZrO2 65% SiO2 35% |
| 5 |
Density |
3.86g/cm3 |
| 6 |
Vickers hardness |
643~785HV |
| 7 |
Dust Pollution |
NO |
| 8 |
Metal contamination |
NO |
| 9 |
Cycle index |
many times |
| 10 |
Service life |
long |
| 11 |
Equipment wear |
low |